MTC412

Med Temp Cure, High Temp Service OOA

Let’s Discuss your application needs

Key Features & Benefits

Key Feature High service temperature and out of autoclave processing

Application High service temp and Out of Autoclave processing typically for Aerospace applications

Initial Cure Temp 80°C- 150°C

Initial Cure Time 16 Hours- 1 Hours

Post Cure Option Yes

Outlife 28 days at 20°C

TG Onset* 170°C -DMA

TG Peak* 190°C -DMA

Toughened Yes

Cure Autoclave and Oven

Availability All sites

MTC412 epoxy prepreg is designed to give enhanced toughness and higher service temperature with the flexibility of out of autoclave manufacture. It is a sided system giving great flexibility in component manufacture. MTC412 is a highly toughened system that can be supplied with any standard reinforcement to meet your cost and manufacturing requirements.

Why choose this material

MTC412 has been optimised for Out of Autoclave processing to deliver structural parts with a high service temperature. It is also a sided system to give you greater flexibility when manufacturing components.

Supplied with SHD's renowned service, including:

Short two-week lead times and low MOQs
Exceptional product quality
First class technical support
Excellent customer service
The same manufacturing equipment and processes across all sites

Aerospace

Advanced composites specified across major commercial aircraft today

Find out more

Technical Guidance Information

This material should be kept frozen at -18°C (0°F). It must be kept sealed in a polythene bag which must not be opened until fully thawed to room temperature. If the material is not fully used, then the material must be resealed in the polythene bag to prevent moisture absorption.

This material contains epoxy resin which can cause allergic reactions with skin contact and must avoid repeated and prolonged skin contact.

Please refer to the product Safety Data Sheet before using this material. The following precautions must be taken when using epoxy resin prepregs:

Overalls must be worn
Impervious gloves must be worn
Curing schedule is meant to be as a guide only and is subject to local conditions
To avoid exotherm, particular care must be taken with thick laminates
Ramp rates must not exceed 3.0°C (5.4°F)/min during initial cure and 0.3°C (0.5°F)/min during post cure