BMI-1SC

BMI Tooling & Component

Let’s Discuss your application needs

Key Features & Benefits

Key Feature High durability aerospace tooling

Application High temp, high durability Aerospace tooling

Initial Cure Temp 365°F

Initial Cure Time 2 Hours

Post Cure Option Yes

Outlife 30 days at 70°F

TG Onset* 662°F -DMA

TG Peak* 671°F -DMA

Toughened No

Cure Autoclave

Availability All sites

BMI-1SC prepreg resin system is designed for use in high temperature tooling or components.

It has been formulated to give very high service temperatures without compromising performance and may provide extended tool life compared to lower Tg alternatives.

Why choose this material

BMI-1SC provides a highly durable tool, giving you extended tool life to maximise production efficiency. It can also be used to manufacture high temperature structural components.

Supplied with SHD's renowned service, including:

Short two-week lead times and low MOQs
Exceptional product quality
First class technical support
Excellent customer service
The same manufacturing equipment and processes across all sites

Aerospace

Advanced composites specified across major commercial aircraft today

Find out more

Technical Guidance Information

This material should be kept frozen at -18°C (0°F). It must be kept sealed in a polythene bag which must not be opened until fully thawed to room temperature. If the material is not fully used, then the material must be resealed in the polythene bag to prevent moisture absorption.

This material contains resin which can cause allergic reactions with skin contact and must avoid repeated and prolonged skin contact.

Please refer to the product Safety Data Sheet before using this material. The following precautions must be taken when using epoxy resin prepregs:

Overalls must be worn
Impervious gloves must be worn
Curing schedule is meant to be as a guide only and is subject to local conditions
To avoid exotherm, particular care must be taken with thick laminates